Reflection measurements in the 25–35 nm region were made for Mg/SiC and Mg/Y2O3 multilayers kept in a low-humidity atmosphere for 4 or 5 years. Aged Mg/SiC multilayers keep their reflectances, and the reflectance value at 31.2 nm is 0.44 at 10° of the normal angle of incidence. Aged Mg/Y2O3 multilayers change reflectance as top layer materials, and the best value at 30.1 nm is 0.40 at 10°. Reflection measurements are also made for Mg-based multilayers that are annealed from room temperature to 400 °C at 50 °C intervals. Both multilayers keep their reflectance at annealing temperatures of 200 °C. These results suggest that both Mg-based multilayers can be applied to practical optics.
© 2005 Optical Society of America
Full Article | PDF ArticleMore Like This
Mónica Fernández-Perea, Regina Soufli, Jeff C. Robinson, Luis Rodríguez De Marcos, Jose A. Méndez, Juan I. Larruquert, and Eric M. Gullikson
Opt. Express 20(21) 24018-24029 (2012)
Jingtao Zhu, Zhanshan Wang, Zhong Zhang, Fengli Wang, Hongchang Wang, Wenjuan Wu, Shumin Zhang, Da Xu, Lingyan Chen, Hongjun Zhou, Tonglin Huo, Mingqi Cui, and Yidong Zhao
Appl. Opt. 47(13) C310-C314 (2008)
Jingtao Zhu, Sika Zhou, Haochuan Li, Qiushi Huang, Zhanshan Wang, Karine Le Guen, Min-Hui Hu, Jean-Michel André, and Philippe Jonnard
Appl. Opt. 49(20) 3922-3925 (2010)